Chemtainer.com offers you a selection of materials that are by far the best suited for molded tanks and containers for use with aggressive corrosive chemicals as well as food products. Our 35 plus years of experience in rotational molding, combined with our professional staff of chemical, mechanical and plastics engineers, enables us to provide you with the highest quality rotationally molded tanks and containers available in the industry.
The following is a brief description of these materials:
A high quality thermoplastic that has outstanding resistance to both physical and chemical attack. The overall general toughness and excellent chemical resistance to a wide array of wet and dry industrial chemicals and food products make polyethylene ideally suited for storage tanks and containers.
Polyethylene is translucent and its natural color ranges from slightly off white to creamy yellow, depending on wall thickness and type. Ultraviolet light stabilizers are added for use in outdoor applications. Colors are available on request for a nominal up charge. BPA-Free Material.
Linear Polyethylene is available as low, medium and high density. Most products offered in this catalog are molded of linear medium density polyethylene (LMDPE) and linear high density polyethylene (LHDPE). They have superior mechanical properties, high stiffness, excellent low temperature impact strength and excellent environmental stress crack resistance. The linear polyethylene used by Chem-Tainer meets specifications contained in FDA regulation 21CFR177.1520 (c) 3.1 and 3.2 and so may be used as an article or a component of articles intended for use in contact with food, subject to any limitations in the regulations. Maximum operating temperature for linear polyethylene is 140° F. BPA-Free Material.
Crosslinkable polyethylene is a high density polyethylene that contains a crosslinking agent which reacts with the polyethylene during molding, forming a crosslinked molecule similar to a thermoses plastic. This reaction improves toughness and environmental stress crack resistance. Crosslinked Polyethylene (XLPE) is not weldable and does not meet FDA requirement 21CFR177.1520. Maximum operating temperature of crosslinked polyethylene is 150° F.
Polypropylene is a rigid plastic that has a higher operating temperature limit than polyethylene: 212° F. It offers good chemical resistance, has a high resistance to stress crack, and is autoclavable. Polypropylene (PP) is not recommended for applications in sub-freezing temperature or where high impact strength is needed. A rough, irregular interior surface is common characteristic of molded polypropylene.
Continued or prolonged service with contents at elevated temperatures can shorten the life of a tank. The effects of the temperature will depend on the chemical content and its specific gravity, tank size and configuration, material of construction, wall thickness and if there are any external supports on the tank.
Unprotected thermoplastics exposed to sunlight for an extended period of time, absorb ultraviolet (UV) light, which can cause discolorations, embrittlement and eventual cracking. Fluorescent lighting has a similar effect. Elevated temperatures can accelerate the embrittling process. Chem-Tainer products are molded from materials utilizing the latest technology for UV stabilizers which greatly reduce the harmful effects of UV light. For greater protection, keep tanks out of direct sunlight or order dark colored tanks which will further retard the effect of UV light.
Certain surface active materials, although they have no chemical effect on polyethylene, can accelerate its cracking when under stress, such as liquid detergents and ultra pure water- (see our chemical compatibility Chart on pages 46 – 49.) Elevated temperatures tend to accelerate the cracking. Although all polyethylenes are subject to stress cracking, some are more resistant to it than others. The degree of stress on the plastic has a direct bearing on its resistance, therefore a tank and system should be designed to minimize stress. Chemtainer.com tanks are molded visually stress free, employing materials that are highly resistant to environmental stress cracking, and hence are less prone to cracking than fabricated tanks. Stress cracking agents are surface active materials. Proper care should be taken to reduce stress at fillings, bands, tie down lugs, etc.
|Maximum Service Temp||140 F (60 C)||150 F (65 C)||212 F (100 C)|
|Chemical Resistance||Very Good||Very Good||Very Good|
|Stress Crack Resistance||Excellent||Excellent||Excellent|
|General Toughness||Very Good||Very Good||Fair|
|Color||WH Translucent||Off WH Trans||Off WH Opaque|
|Physical Properties (Nominal Values)||Linear||XLPE||PP|
|Density (gm/cc) ASTM:D1505||0.937-0.942||0.937-0.942||0.901-0.905|
|Environmental Stress Cracking (F-50hrs) ASTIM:D1693||>1,000||>1,000||>1,000|
|Tensile Strength ASTIM:D638 Ultimate 2″/Min (PSI) Type IV||2,600||2,600||3,000|
|Elongation at Break ASTIM:D638 2″/Min(%) Type IV||450||450||5|
|Flexural Modulus (PSI) ASTIM:D790||100,000-110,000||100,000-110,000||90,000-100,000|
|Brittleness Temp ASTIM:D746||<-94F (-70 C)||-180 F (-118 C)||32 F (0 C)|
|VICAT Softening Temp ASTIM:D152B||240F||240F||300F|